Details
Chemical Formula:Li7-xLa3Zr2-xTaxO12（x=0.4～0.7）
| Product Code | MA-EN-SS-0144 | |
| Test Items | Test results | Method |
| Appearance | White powder, uniform and free of foreign matter | Visual inspection |
| Structure | Cubic phase, conforms to PDF#80-0457 | X-ray diffractometer |
| Particle Size - D50 (μm) | 0.56 | Particle size analyzer |
| Moisture (wt%) | 0.2 | Moisture tester |
| Ionic Conductivity (mS/cm) | 0.78 | Sintered ceramic pellet, tested by electrochemical workstation at 25℃ |
| Test Conditions 1.XRD Test: Sample preparation in a low-humidity environment, tested over a 2θ range of 10–90°. 2.Ionic Conductivity Test: Take an appropriate amount of powder, pour it into a 10mm-diameter pellet die, press at 350MPa to form a pellet, then sinter at 1200℃ for 4h to obtain a ceramic pellet. Grind and polish the pellet with 400–800–2000 grit sandpaper, then sputter gold on both sides. Note: After gold sputtering, the side surfaces must be ground clean. Test EIS with an electrochemical workstation: frequency 7MHz–1Hz, amplitude 10mV. (The sintering schedule is for reference only; the optimal sintering parameters can be adjusted according to the specific sintering process, which has a significant impact on the ionic conductivity of the test sample.) 3.Electronic Conductivity Test: Test i-t on the sintered ceramic pellet: constant voltage 0.5V, test duration 1800s. 4.Particle Size Test: Laser diffraction, disperse the powder with ultrasound for 3min. |
||
XRD Pattern
Electrochemical Impedance Plot