LPSC Sulfide Solid Electrolyte (Li6PS5Cl), 10-20 μm

Name: Gel Chromatography System
Brand: Canrd

$211.43

Número do item:MA-EN-SS-013201

Especificações

✓ Selecionado: 10g

Quantidade

Garantia de Qualidade

Venda direta da fábrica

Envio mundial

Details

Visão Geral

Especificações

Detalhes

This sulfide solid electrolyte, lithium-phosphorus-sulfur-chlorine (Li₆PS₅Cl, LPSC), is developed as a high-performance ion-conductive material for all-solid-state battery research. With a median particle size (D50) around 15 µm and a crystalline main phase of Li₇PS₆, it appears as a grayish-white powder. The material exhibits an ionic conductivity of 4.18 mS/cm at 25 °C under 350 MPa, coupled with a very low electronic conductivity of 7.18 nS/cm, making it suitable as a solid electrolyte layer or as a component in composite cathodes. Its well-defined particle size distribution supports consistent processing in pellet formation and slurry-based electrode fabrication. This LPSC system is particularly relevant for studies aiming to improve interfacial stability and ionic transport in sulfide-based solid-state batteries.

Test Items		Test result	Method
Appearance		Grayish-white powder, uniform and without any abnormalities.	Visual inspection.
Phenomena		Sulfur-silver-germanium ore Main crystal phase：Li7PS6	X-ray diffraction instrument
Particle size	D10(μm)	2.231	Particle size analyzer
	D50(μm)	15.083
	D90(μm)	46.552
Ionic conductivity (mS/cm)		4.18	Pressed into sheets at 25°C and 350MPa, electrochemical impedance spectroscopy was performed.
lectron conductivity (nS/cm)		7.18	Pressed into sheets at 25℃ and 350MPa, electrochemical impedance spectroscopy was performed.
Test conditions: (1) XRD test: Samples were prepared in an inert atmosphere glove box, avoiding polar solvent atmospheres. The surface was sealed with polyimide film to isolate air and moisture. (2) Ionic conductivity test: 100 mg of powder was used, a mold diameter of 10 mm was applied, and a pressure of 350 MPa was applied to form a pellet. The pressure was maintained at 350 MPa. EIS test: frequency 1 MHz ~ 1 Hz, amplitude 10 mV. (3) Electronic conductivity test: 100 mg of powder was used, a mold diameter of 10 mm was applied, a pressure of 350 MPa was applied, and the pressure was maintained at 350 MPa. i-t test: constant voltage 0.5 V, test time 1800 s.