Lithium-ion Battery Cathode Electrode Sheet (LFP Lithium Iron Phosphate LF07)

$75.51

Número do item:LF07XX

Especificações

✓ Selecionado: 5 pcs/pack on one side (Calendered)

Quantidade

Garantia de Qualidade

Venda direta da fábrica

Envio mundial

Details

Visão Geral

Detalhes

Specification Parameters

Item Specification / Value

Coating Thickness

Current Collector Areal Density (mg/cm²) 3.50

Electrode Sheet Size 10 × 10

Current Collector Thickness (μm) 14 (Carbon-Coated Aluminum Foil)

Active Material Content 91.5%

Compatible Electrode Sheet Models for Full-Cell Assembly (N/P Ratio) SM02XX (1.12); LT01XX (1.13); SC02XX (1.05)

Electrode Compaction Density (g/cc) 1.50–2.00 (For uncalendered electrode sheets, no compaction density value is provided; calculate it independently.)

Active Material Lithium Iron Phosphate (High Compaction)

Current Collector Type Carbon-Coated Aluminum Foil

Shelf Life 6 months (stored in vacuum-sealed packaging); use within 1 month after opening

Recommended Electrolyte KLD-LFP01

Lithium Iron Phosphate Electrode Sheet

Electrode Sheet Code LF07XX

Active Material Specific Capacity (mAh/g) 150 (2.50–4.20 V)

Test Condition Description Room temperature 25°C; rest for 4 h; charge at 0.1C (CC) to 4.20 V; CV charge at 4.20 V to 0.02C; rest for 3 min; discharge at 0.1C (CC) to 2.50 V; rest for 3 min

Test Conditions Room temperature 25°C, 0.1/0.1C, 2.50–4.20 V

Areal Capacity (mAh/cm²) 1.69

Coating Areal Density (mg/cm²) 12.30 (Tolerance: ±2.0%)

Recommendations for Use 1. If the electrode sheet has not been calendered, it generally needs to be calendered before punching and drying. The minimum value in the Electrode Compaction Density row of this table may be used as a reference. 2. Drying conditions: 85–105°C for 4 h. If vacuum drying is used, perform two gas exchanges. 3. The active material mass shall be determined based on the actual weighing result of each punched disc.

Item	Specification / Value
Coating Thickness
Current Collector Areal Density (mg/cm²)	3.50
Electrode Sheet Size	10 × 10
Current Collector Thickness (μm)	14 (Carbon-Coated Aluminum Foil)
Active Material Content	91.5%
Compatible Electrode Sheet Models for Full-Cell Assembly (N/P Ratio)	SM02XX (1.12); LT01XX (1.13); SC02XX (1.05)
Electrode Compaction Density (g/cc)	1.50–2.00 (For uncalendered electrode sheets, no compaction density value is provided; calculate it independently.)
Active Material	Lithium Iron Phosphate (High Compaction)
Current Collector Type	Carbon-Coated Aluminum Foil
Shelf Life	6 months (stored in vacuum-sealed packaging); use within 1 month after opening
Recommended Electrolyte	KLD-LFP01

Packaging, Transportation and Storage

1.Store under vacuum or double‑seal with self‑sealing bags inside a glove‑box. Especially for high‑nickel and sodium‑ion cathode materials, improper storage will increase the internal resistance of batteries.

2.The electrode sheets are un‑calendered. Please calender the electrodes according to the suggested compaction density.

3.The coating areal density shall be determined by actual weighing, which excludes the current collector.

4. Actual mass of active material
(mg) = (disc weight (mg) - current- collector areal density (mg/cm2) x disc area (cm2))
5. Theoretical mass of active material
(mg) = coating areal density (mg/cm2) X active material mass fraction X disc area (cm2)
6. Theoretical areal capacity
specific capacity (mAh/g)+ 1000
(m Ah/cm2) = coating areal density (mg/cm2) X active material mass fraction Xspecific capacity (mAh/g)+ 1000

7.Specific capacity shall be calculated based on the gravimetrically measured active‑material mass. Given the tolerance of coating areal density, actual weighing shall prevail.

8.Crease note: Single‑sided electrodes tend to curl after calendering. Flattening for packaging may introduce creases.

Precisa de suporte R&D?

Explore categorias principais de produtos e ligue materiais de bateria aos servicos R&D da Canrd.

Materiais experimentais

Categoria

Catodos, anodos, eletrolitos, separadores e outros materiais para investigacao de baterias.

Comprar materiais de catodo, anodo e eletrolito →

Equipamento de laboratorio

Categoria

Equipamento de laboratorio de baterias para linhas piloto, fixtures e fluxos de teste.

Ver equipamento de laboratorio de baterias →

Eletrodos e celulas

Categoria

Eletrodos personalizados, celulas secas e componentes de celulas para validacao R&D.

Ver eletrodos e celulas de bateria personalizados →

Eletrolito de sodio

Categoria

Opcoes de eletrolito de ioes de sodio para investigacao e validacao de baterias de sodio.

Comprar eletrolitos de bateria de sodio →

Servicos R&D

Servico

Servicos completos de R&D de baterias, da avaliacao de materiais a fabricacao de celulas e analise de falhas.

Explorar servicos R&D da Canrd →

Avaliacao de materiais

Servico

Caracterizacao, testes eletroquimicos e avaliacao de compatibilidade para materiais de bateria.

Avaliar os seus materiais de bateria →

Fabricacao de eletrodos

Servico

Folhas e rolos de eletrodos personalizados conforme a quimica e processo alvo.

Solicitar fabricacao de eletrodos →

Fabricacao de celulas

Servico

Celulas secas, celulas montadas e formatos personalizados para validacao R&D.

Construir celulas de investigacao personalizadas →

Contacto

Pagina

Peca a Canrd para combinar produtos, materiais e servicos para o seu projeto.

Obter suporte de produto e R&D →

Pedir orçamento

Enviar comentários

	Lithium Iron Phosphate Electrode Sheet
Electrode Sheet Code	LF07XX
Active Material Specific Capacity (mAh/g)	150 (2.50–4.20 V)
Test Condition Description	Room temperature 25°C; rest for 4 h; charge at 0.1C (CC) to 4.20 V; CV charge at 4.20 V to 0.02C; rest for 3 min; discharge at 0.1C (CC) to 2.50 V; rest for 3 min
Test Conditions	Room temperature 25°C, 0.1/0.1C, 2.50–4.20 V
Areal Capacity (mAh/cm²)	1.69
Coating Areal Density (mg/cm²)	12.30 (Tolerance: ±2.0%)
Recommendations for Use	1. If the electrode sheet has not been calendered, it generally needs to be calendered before punching and drying. The minimum value in the Electrode Compaction Density row of this table may be used as a reference. 2. Drying conditions: 85–105°C for 4 h. If vacuum drying is used, perform two gas exchanges. 3. The active material mass shall be determined based on the actual weighing result of each punched disc.