Silicon-Carbon Alloy (1200)

$90.61

Numéro d'article:MA-EN-AN-000401

Spécifications

✓ Sélectionné: 20g

Quantité

Assurance qualité

Vente directe usine

Livraison mondiale

Details

Aperçu

Spécifications

Détails

This Silicon-Carbon Alloy (1200) is designed for use as a lithium-ion battery anode material, with a surface carbon coating to enhance rate capability and cycling stability. Based on the provided specifications, the material exhibits a D50 particle size around 13 µm and a tap density of 0.89 g/cm³, supporting practical electrode processing. Electrochemical testing shows an initial reversible capacity of 1343.8 mAh/g and an initial Coulombic efficiency of 83.8%, indicating high capacity with reasonable first-cycle loss. For half-cell evaluation, it is recommended to use carbon-coated copper foil and NCM electrolyte (KLD-1230C), with electrode baking at 85 °C for 4 hours. The product should be stored under sealed conditions. This material is well-suited for energy materials research and anode development.

Storage Requirement: Materials must be stored in a sealed container.

Electrolyte Used for Testing: Si/C Electrolyte (KLD-Si01)

Recommended Current Collector: Carbon-Coated Copper Foil

Baking conditions for electrode: Bake at 85 ℃ for 4 hours

Lithium ion anode electrode material, surface coated with carbon, excellent rate performance, good cycling performance

Physical and chemical properties

No.	Category	Test Item	Unit	Specification	Test Result
1	Physical Properties	Particle Size Distribution - D10	(μm)	5.0 ± 3.0	4.23
2		Particle Size Distribution - D50	(μm)	13.0 ± 2.0	13.10
3		Particle Size Distribution - D90	(μm)	≤ 30.0	29.89
4		BET Specific Surface Area	(m²/g)	≤ 6.0	4.38
5		Tap Density (TD)	(g/cm³)	≥ 0.7	0.89
6	Electrochemical Performance	Initial Reversible Capacity	(mAh/g)	≥ 1150.0	1343.8
7		Initial Coulombic Efficiency	(%)	≥ 83.0	83.8