Silicon Suboxide (1400) - A

Name: Silicon Suboxide (1400) - A
Brand: Canrd
Price: 120.82 USD
Availability: InStock

$120.82

Número de artículo:MA-EN-AN-003701

Especificaciones

✓ Seleccionado: 20g

Garantía de calidad

Venta directa de fábrica

Envío mundial

Details

Descripción general

Especificaciones

Detalles

This pre-lithiated silicon oxide material, designated Silicon oxide (1400) - A, is developed as a high-capacity anode material for lithium-ion batteries. It features a sub-micron particle size distribution (D50 around 8 μm) with a low BET specific surface area of ≤0.9 m²/g, facilitating good processability and electrode coating uniformity. Electrochemical testing in half cells using NCM electrolyte demonstrates a first reversible capacity exceeding 1400 mAh/g at 1.5 V cutoff, with a first coulombic efficiency of at least 88%. The material is free from a distinct silicon peak and shows low trace metal and magnetic substance contamination, supporting stable cycling. It is typically applied in advanced battery research requiring high energy density anodes. The product is vacuum-sealed in aluminum-plastic film and should be stored in a cool, dry environment to maintain its pre-lithiated state.

Lithium ion anode electrode material, pre lithiated silicon oxide, no silicon peak, with the characteristics of high capacity and high first effect

Physical and chemical properties

No.	Test Item		Unit	Specification	Test Result
1	Trace Metal Content	Fe (Iron)	ppm	≤10.0	6.23
2		Cu (Copper)	ppm	≤3.0	1.02
4	Magnetic Substances	Fe+Co+Cr+Ni+Zn	ppm	≤0.5	0.38
5	Physical Properties (Particle Size Distribution)	D10	μm	5.0±1.0	4.62
6		D50	μm	8.0±2.0	8.12
7		D90	μm	≤15.0	13.26
8	Physical Properties	BET Specific Surface Area	m²/g	≤0.9	0.86
9		Tap Density (TD)	g/cm³	≥1.0	1.12
11	Electrochemical Performance	1.5V First Reversible Capacity	mAh/g	≥1400.0	1486.5
12		1.5V First Coulombic Efficiency	%	≥88.0	88.6
13		0.8V First Reversible Capacity	mAh/g	≥1200.0	1365.2
14		0.8V First Coulombic Efficiency	%	≥80.0	81.3