Sulfur carbon composite cathode material (sulfur content 75%)

The material needs to be vacuum sealed for storage

The drying temperature should not be too high, 50-60 ℃ is suitable

The electrolyte used during testing is lithium sulfur electrolyte KLD-S46

Baking conditions for electrode: Bake at 50 ℃ for 4 hours

Usage suggestion:

1. Environment: Operate in a regular environment;

2. Suggested ratio: sulfur carbon: Keqin black: HSV900=91:3:6;

3. Temperature: During the pulp making process, the temperature should be controlled to avoid heating up the pulp;

4. Current collector: It is recommended to use carbon coated aluminum foil as the current collector;

5. Drying temperature: 50-60 ℃ is suitable. To ensure complete volatilization of NMP, it is recommended to bake overnight;

6. The recommended baking temperature after punching is 50-60 ℃, with a baking time of about 4 hours;

7. Suggested electrolytes: KLD-S17, KLD-S03, KLD-S46;

8. Recommended voltage range: 1.8-2.8V;

9. Nominal gram capacity: 850mAh/g