Silicon-Carbon Electrode Sheet SC02XX
Details
This product must be tested according to Canrd recommended testing methods and electrolytes to achieve the desired performance.
Because testing methods and electrolytes significantly impact battery performance, changing the testing method or electrolyte may degrade electrode performance. Please verify this information before purchasing.
Electrode Sheet Technical Data Sheet (SC02XX - Si/C 420 Electrode)
| Parameter | Specification |
|---|---|
| Slurry Areal Density (mg/cm²) | 7.25 |
| Electrode Sheet Size | 10 × 10 cm |
| Current Collector Thickness (μm) | 9 (Carbon-coated Cu foil) |
| Active Material Ratio | 95.00% |
| Compacted Density (g/cc) | 1.10 (Not compacted; value needs self-calculation) |
| Active Material | Si/C 1800 (5%) + Graphite (95%) |
| Recommended Electrolyte | KLD-Si01 |
| Electrode Name | Si/C 420 Electrode |
| Electrode Code | SC02XX |
| Specific Capacity (mAh/g) | 420 (0.005–2.000 V) |
| Areal Capacity (mAh/cm²) | 1.9 |
| Coating Areal Density (mg/cm²) | 4.80 (Tolerance ±2.0%) |
Usage Recommendations
-
If the electrode is not compacted, it should be compacted before punching and baking. (Reference minimum value above for compacted density.)
-
Baking conditions: 85–105°C for 4 hours.
If vacuum baking, replace the air twice. -
Active material mass should be weighed for each circular electrode individually for accurate calculation.
Compatible Full Cell Electrode Models (N/P Ratio ≈ 1.09)
SY13XX, SY25XX, SY33XX, LF06XX, LC02XX
Test Conditions
-
Ambient temperature: 25°C, rest for 4 h
-
Discharge: 0.10C / 0.09C / 0.08C / ... / 0.01C (constant current) to 0.005 V
-
Rest for 3 min
-
Charge: 0.1C (constant current) to 2.00 V
-
Rest for 3 min
Shelf Life
-
6 months in vacuum-sealed storage
-
Use within 1 month after opening
Capacity Measurement Conditions
-
25°C
-
0.10 / 0.09 / 0.08 / 0.07 / 0.06 / 0.05 / 0.04 / 0.03 / 0.02 / 0.01 C DC discharge to 0.005 V
-
0.1 C CC charge to 2.00 V
This product must be tested according to Canrd recommended testing methods and electrolytes to achieve the desired performance.
Because testing methods and electrolytes significantly impact battery performance, changing the testing method or electrolyte may degrade electrode performance. Please verify this information before purchasing.
Electrode Sheet Technical Data Sheet (SC02XX - Si/C 420 Electrode)
| Parameter | Specification |
|---|---|
| Slurry Areal Density (mg/cm²) | 7.25 |
| Electrode Sheet Size | 10 × 10 cm |
| Current Collector Thickness (μm) | 9 (Carbon-coated Cu foil) |
| Active Material Ratio | 95.00% |
| Compacted Density (g/cc) | 1.10 (Not compacted; value needs self-calculation) |
| Active Material | Si/C 1800 (5%) + Graphite (95%) |
| Recommended Electrolyte | KLD-Si01 |
| Electrode Name | Si/C 420 Electrode |
| Electrode Code | SC02XX |
| Specific Capacity (mAh/g) | 420 (0.005–2.000 V) |
| Areal Capacity (mAh/cm²) | 1.9 |
| Coating Areal Density (mg/cm²) | 4.80 (Tolerance ±2.0%) |
Usage Recommendations
-
If the electrode is not compacted, it should be compacted before punching and baking. (Reference minimum value above for compacted density.)
-
Baking conditions: 85–105°C for 4 hours.
If vacuum baking, replace the air twice. -
Active material mass should be weighed for each circular electrode individually for accurate calculation.
Compatible Full Cell Electrode Models (N/P Ratio ≈ 1.09)
SY13XX, SY25XX, SY33XX, LF06XX, LC02XX
Test Conditions
-
Ambient temperature: 25°C, rest for 4 h
-
Discharge: 0.10C / 0.09C / 0.08C / ... / 0.01C (constant current) to 0.005 V
-
Rest for 3 min
-
Charge: 0.1C (constant current) to 2.00 V
-
Rest for 3 min
Shelf Life
-
6 months in vacuum-sealed storage
-
Use within 1 month after opening
Capacity Measurement Conditions
-
25°C
-
0.10 / 0.09 / 0.08 / 0.07 / 0.06 / 0.05 / 0.04 / 0.03 / 0.02 / 0.01 C DC discharge to 0.005 V
-
0.1 C CC charge to 2.00 V
This product must be tested according to Canrd recommended testing methods and electrolytes to achieve the desired performance.
Because testing methods and electrolytes significantly impact battery performance, changing the testing method or electrolyte may degrade electrode performance. Please verify this information before purchasing.
Electrode Sheet Technical Data Sheet (SC02XX - Si/C 420 Electrode)
| Parameter | Specification |
|---|---|
| Slurry Areal Density (mg/cm²) | 7.25 |
| Electrode Sheet Size | 10 × 10 cm |
| Current Collector Thickness (μm) | 9 (Carbon-coated Cu foil) |
| Active Material Ratio | 95.00% |
| Compacted Density (g/cc) | 1.10 (Not compacted; value needs self-calculation) |
| Active Material | Si/C 1800 (5%) + Graphite (95%) |
| Recommended Electrolyte | KLD-Si01 |
| Electrode Name | Si/C 420 Electrode |
| Electrode Code | SC02XX |
| Specific Capacity (mAh/g) | 420 (0.005–2.000 V) |
| Areal Capacity (mAh/cm²) | 1.9 |
| Coating Areal Density (mg/cm²) | 4.80 (Tolerance ±2.0%) |
Usage Recommendations
-
If the electrode is not compacted, it should be compacted before punching and baking. (Reference minimum value above for compacted density.)
-
Baking conditions: 85–105°C for 4 hours.
If vacuum baking, replace the air twice. -
Active material mass should be weighed for each circular electrode individually for accurate calculation.
Compatible Full Cell Electrode Models (N/P Ratio ≈ 1.09)
SY13XX, SY25XX, SY33XX, LF06XX, LC02XX
Test Conditions
-
Ambient temperature: 25°C, rest for 4 h
-
Discharge: 0.10C / 0.09C / 0.08C / ... / 0.01C (constant current) to 0.005 V
-
Rest for 3 min
-
Charge: 0.1C (constant current) to 2.00 V
-
Rest for 3 min
Shelf Life
-
6 months in vacuum-sealed storage
-
Use within 1 month after opening
Capacity Measurement Conditions
-
25°C
-
0.10 / 0.09 / 0.08 / 0.07 / 0.06 / 0.05 / 0.04 / 0.03 / 0.02 / 0.01 C DC discharge to 0.005 V
-
0.1 C CC charge to 2.00 V